Mold having a breathable release sheet across the top

ABSTRACT

Mold, particularly for rigid polyurethane foam articles having finished textured surfaces on all sides thereof comprising a female mold having a recess into which the unreacted and unblown resin system is deposited and a cover for closing the mold together with a release sheet structure disposed therebetween exhibiting sufficient gas porosity to enable complete venting of air displaced by the rising foam in the production of a finished surface thereat and method of molding therewith.

United States Patent Wilheim Oct. 29, 1974 [54] MOLD HAVING A BREATHABLE RELEASE 3,108,850 10/1963 Brandt 264/98 X SHEET ACROSS THE op 3,43i,33l 3/1969' Piacus et al 425/8l4 X Inventor:

[76] Martin J. Wilheim, 52 Elm Ave.,

Lurchmont, NY. 10538 Filed: July 6, 1973 Appl. No.: 377,116

Related US. Application Data Continuation of Ser. No. 101,823, Dec. 28, 1970, abandoned.

US. Cl. 425/113, 425/85 Int. Cl B28b 7/36 Field of Search... 249/113, 115; 425/85, 817 R References Cited UNITED STATES PATENTS 2,983,570 5/1961 Lux 264/214 X Primary Examiner-R. Spencer Annear Attorney, Agent, or FirmElliot A. La'ckenback [5 7] ABSTRACT Mold, particularly for rigid polyurethane foam articles having finished textured surfaces on all sides thereof comprising a female mold having a recess into which the unreacted and unblown resin system is deposited and a cover for closing the mold together with a release sheet structure disposed therebetween exhibiting sufficient gas porosity to enable complete venting of air displaced by the rising foam in the production of a finished surface thereat and method of molding there with.

8 Claims, 2 Drawing Figures MOLD HAVING A BREATHABLE RELEASE SHEET ACROSS THE TOP This is a continuation of application Ser. No. ll,823, filed Dec. 28, 1970, now abandoned.

This invention relates to methods and apparatus for molding foamable materials.

It is a primary object of the present invention to provide methods and apparatus for molding foamable materials so as to produce finished surfaces on all sides thereof.

Another primary object of the present invention, in addition to the foregoing object, is to provide such methods and apparatus wherein the surfaces produced may be selectively smooth, textured, and/or printed or colored.

Another primary object of the present invention, in addition to each of the foregoing objects, is the provision of such methods and apparatus wherein the resultant products simulate hand-carved wood or other surfaces or materials.

Yet another primary object of the present invention, in addition to each of the foregoing objects, is the provision of such methods and apparatus for molding, particularly rigid urethane foams.

Yet still another primary object of the present invention, in addition to each of the foregoing objects, is the provision of methods and apparatus for molding of foams within a cavity having means of sufficient gas porosity for venting to enable the foam to fully fill the cavity while preventing the exudation of the foam material therefrom.

Yet still further, is is another primary object of the present invention, in addition to each of the foregoing objects, to provide methods and apparatus for molding of foams within molds comprising a cavity and a cover therefor together with a sheet of material having one or more layers beneath the cover non-adherent to the foam and of sufficient gas porosity to vent the cavity during foaming so that the foam may fully and completely fill the cavity and produce a finished and/or hard-skinned, smooth or textured but void or bubblefree surface against the cover.

Another primary object of the present invention, in addition to each of the foregoing objects is the provision of reusable breathable release papers for molding urethane foams and the like which are non-adherent to the foam and which may produce a finished surface thereto free of voids or defects and which may be hardskinned and selectively smooth or textured and/or printed with a desired pattern.

Another and yet still further primary object of the present invention, in addition to each of the foregoing.

objects, is the provision of such methods and apparatus wherein the release structure comprises a smooth, creped or embossed paper backing sheet coated or impregnated with a release material for contact with the foam.

Still another and yet further primary object of the present invention, in addition to each of the foregoing objects, is the provision of such methods and apparatus wherein the release material comprises quilon, aqueous silicone or a multi-layered structure such as a layer of a plastic; for example, a polyolefrn such as polyethylene or avinyl resin such as polyvinyl acetate coated with a layer of quilon or silicone such as dimethylpolysiloxane.

A still further primary object of the present invention, in addition to each of the foregoing objects, is the provision in a mold for rigid urethane foams, of a creped paper sheet having sufficient gas porosity to enable complete venting of the mold chamber during foaming while precluding exudation of the foam and covered with a release material for disposing beneath the mold cover and the formation of molded articles finished on all sides.

Yet still another primary object of the present invention,- in addition to each of the foregoing objects, is the objects, is the provision of breathable, reusable release 5 papers against which urethane foam may be molded to produce a fully finished surface thereto.

The invention resides in the combination, construction, arrangement and disposition of the various component parts and elements incorporated in improved molds constructed in accordance with the principles of this, invention and in methods of molding therewith. The present invention will be better understood andobjects and important features other than those specifically enumerated above will become apparent when consideration is given to the following details and description, which when taken in conjunction with the annexed drawing describes, discloses, illustrates and shows a preferred embodiment or modification of the present invention and what is presently considered and believed to be the best mode of practicing the principles thereof.

IN THE DRAWING FIG. 1 is a diagrammatic perspective illustration of an exemplary mold and article formed therein in accordance with the present invention and FIG. 2 is a cross-sectional elevational enlarged view of a portion thereof.

Polyurethane foams are now in widespread use by furniture manufacturers, contract molders, etc., to cast mold such products as picture frames, plaques, wooden beams for ceilings, moldings for mirrors, statues, furniture parts and trim, simulated carvings, clock housings and many other ornate or finely detailed products. Rigid urethane foam, when poured into a female mold cavity made to the exact configuration of the desired part, faithfully reproduces the contours of that mold and cures to form a toughskinned piece which can be finished and worked just like wood. Texture and grain patterns can be reproduced on the surface and deep undercuts can be molded into the piece for added authenticity.

The mold may be made from a master which can be an original piece especially created by a skilled artisan in wood or metal, or the master can be the exact item that is required for reproduction in dense foam. Such molds may be made of liquid latex, silicone rubbers,

castable urethanes, elastomers, etc. Various techniques have been developed for mold making.

Once the mold has been produced, the following steps are customary to make a foam molded part.

1. A release agent and/or a barrier coat may be sprayed over the entire surface of the mold prior to molding each piece. These enable the foam molded part to be easily removed from the mold. The barrier coat, which is normally pigmented, adheres to the foam and becomes a continuous outer surface of the foam part, serving to cover up tiny blisters which might be encountered if the foam were bare. The barrier coat may also serve as a base tonal coat for subsequent finishing. Since the foamed pieces may later be finished or stained the release agent should be either paintable or adapted to be easily removed.

2. A predetermined amount of material from which the foam is generated may then be distributed in the mold. This material or foam system is generally created by blending two liquid components at the time of deposition in the mold which react chemically to provide a self-foaming, self-curing composition. The foam system formula may vary dependent upon the characteristics required in the finished part. Only a portion of the mold is generally filed with the unblown system with the selfrise or blowing characteristics of the foam being utilized to expand the system to completely fill the mold.

3. A cover or lid of a rigid material then has a release material applied to its lower surface and it is then laid or placed on top of the mold cavity, either mechanically or hydraulically on the mold so as to close the cavity and confine the foam during its rise.

4. About 30 to 60 seconds after the foam is poured into the mold, it begins to cream or begin its foaming action. Then the foam begins its rise to fill the cavity of the mold.

5. The foam need only remain in the mold a total, for example, of 8 to minutes until it completes its cream and rise stages and has at least initially cured. Then the lid is removed and the cured part is demolded. If the part is removed after only, for example, 8 to 15 minutes, the cure is not complete and the part is somewhat flexible, enabling it to be more readily demolded.

6. The molded part is then stained, lacquered, or otherwise finished by means conventional to wood finishes.

As indicated above, the foam material deposited in the mold should be carefully metered in an amount which only partially fills the mold to enable the material to rise and expand to completely fill the mold during foaming. The air which is displaced by the rising foam must be vented outwardly of the closed mold and must escape freely or else it will interfere with proper filling of the mold since if any air is entrapped, it will result in defects, such as bubbles, air pockets, or the like, in the finished part. The component parts of the mold itself, including the mold and the lid or backplate are generally impermeable. Where a finished 6th side, that is, the side cast against the lid or backplate is not required, then the lid or backplate can be loosely clamped to the mold and air vented around the periphery. Any exudation of foam into the gap and any air bubbles trapped between the rising foam and the lid or backplate can all be ground off or cut in a flash removal step. Where, however, it is desired that the molded article be finished on all sides, then specific venting means must be provided.

Moreover, since the foam rises generally upwardly and outwardly, but not entirely evenly, it is important that the venting occur substantially entirely across the inner surface of the lid or backplate and venting around the periphery is not sufficient since during the rise or foaming, small pockets of gas, such as indicated at A in FIG. 2 might be trapped to form a bubble or defect in the surface.

Accordingly, in accordance with the present invention, there is provided a layer of material positioned beneath the lid or backplate of the mold having sufficient gas porosity to enable proper venting without exudation of foam and which is rendered non-adherent to the foam.

With particular reference to the drawing, there is shown and illustrated a mold box 10 having a cavity 12 therein having a mold liner 14 disposed therein defining a mold cavity 16 within which a foamed plastic part 18 may be cast. The mold box 10 is provided with a rigid lid or backplate 20 which may be clamped thereto by substantially any desired clamp, mechanical, hydraulic, or the like, to resist the rising foam. Disposed beneath the lid or backplate 20 there may be provided a layered structure 22 which provides the desired characteristics of gas porosity without permitting exudation of the foam material and which is non-adherent thereto. The layered structure 22 may further, as hereinafter pointed out, provide a desired texture or printing, or flat smooth finish to the adjacent surface of the molded article 18.

Moreover, the layered structure 22, in addition to its breathing or gas porosity characteristics, should have sufficient rigidity so as not to sag into the mold cavity. If the layered structure 22 is not sufficiently rigid so that it does sag into the mold cavity, the foam during its rise may pinch the paper, as in the region A of FIG. 2. Yet still further, the surface of the layered structure 22 against which the foam 18 is cast preferably should produce self-skinning or hard surfacing to the resultant article and, preferably, should be capable of texturing the finished article and be re-usable and may be capable of transferring a printed image thereto.

A suitable layered structure 22 for use in the present invention may comprise a creped backing sheet such as paper 28 coated with a release material on the side in contact with the adhesive. The release material may comprise a layer of a polyolefin 30, such as polyethylene or a vinyl resin such as polyvinyl acetate coated with a silicone coating 32 such as dimethylpolysiloxane. The release material preferably conforms to the surface of the creped backing sheet to provide a crepe surface coated with silicone in contact with the foam 18.

The creped backing sheet 28 may be laminated to a support layer 24 which may comprise, for example, calendered paper by means of glue 26 or other suitable adhesive.

The creped material 23 may also, if desired, be fabricated of other substances having sufficient gas porosity, such as cloth, non-woven fabric, wood veneer, or the like.

The release material may, as pointed out above, comprise polyethylene coated with a silicone but polyethylene alone or silicone alone may also be suitable. However, for maximum effectiveness and economy, the polyethylene-silicone layered structure has been found advantageous since the silicone alone is relatively expensive and too easily absorbed by the backing layer but does aid in providing the desired release characteristics.

The backing sheet may be coated with the release layer and then creped, wrinkled, embossed, printed or the like in the drying state to any desired texture and configuration. For example, the coated backing sheet may be embossed to provide a wood grain pattern. The backing material is preferably creped to -15 percent contraction. However, contraction as high as 50 percent may be used.

Preferably, the backing paper of basic weight of l-8O lbs. per ream is suitable coated with 1-10 lbs. polyethylene per ream over-coated with 0.0l2 lbs. of cured dimethylpolysiloxane solids per ream, then creped or embossed to contract not more than 50 percent of its original width. The backing layer 28 may comprise glassine or clay-filled highly calendered Kraft paper.

The layered structure or breathing paper 22, therefore, preferably has the following characteristics:

1. It has the proper breathing characteristics. It has the right amount of porousity to adequately vent the air from the mold without allowing the foam to bleed through it.

2. It is release treated enabling the paper to be easily peeled off the cured part. The release treatment does not migrate to the foam.

3. As a creped embossing" which simulates a woodgrained appearance. This embossed surface of the paper imparts the same texture to the foam which is molded against it and this embossed outer surface of the part has the desired tough skin.

4. It is rigid enough and therefore does not sag into the mold causing creases.

5. It is suitable for multiple use, i.e., each sheet can be used for three and more moldings and therefore eliminates extra costs in handling and disposal.

Utilizing the present invention, foam parts having all surfaces attractively finished may be produced. Such completely finished or six-sided parts may be used, for example, as a cabinet door with the whole door molded of foam with the back side being free of warp, free of air pockets and having a wood-grain embossing to give it a finished look complementing the other five sides. Even if the sixth side need not be finished for the particular usage to be made, the elimination of any necessity for trim or other finishing steps provides worthwhile savings even where only five-sided parts are required.

The mold liner 14 may comprise any of a number of well-known materials, such as, for example,'silicone rubber, urethane elastomer, or the like, or the molds may comprise rigid materials such as metal. Additionally, an appropriate mold release, such as a lacquer, an emulsifiable wax or thermoplastic film may be applied to the mold. The support layer 24 may comprise a card stock, chip board, cardboard, or substantially any desired material having the requisite rigidity to prevent sag.

In the foregoing specification and the subjoined claims by reference to layered structure, it is specifically intended that such reference include structure having at least one layer. For example, breathable release papers in accordance with the present invention may comprise a first layer laminated to a heavier backing layer or, if such first layer is of sufficient rigidity or thickness to preclude buckling into the mold cavity and thereby preclude the formation of wrinkles therein during crearning or rise of the foam material, the backing layer may be dispensed with.

Moreover, the release material may be applied directly to the support layer, rather than be coated on an intermediate plastic layer. For such direct coating, quilon or silicone solutions may be utilized, for example. Yet further, although urethane foam systems are highly sensitive to moisture, since water reacts therewith to produce carbon dioxide which may result in voids or pockets being formed, an aqueous silicone solution may be used to treat the support layer since the moisture would besufficiently driven off and eliminated during drying.

Finally, as heretofore pointed out, the barrier coat maybe pigmented. Where a variegated or multi-hued finish is desired on the foamed part, the barrier coat may be pigmented to the background or ground color of the desired finish and the release paper or structure may have printed thereon, for example, over the release layer, a pattern or other desired ornamentation which, upon rise of the foam system, will adhere and be transferred thereto from the release layer. Release papers in accordance with the present invention may even be used as a form to enable foaming in place of urethane foam if desired to form finished wall panels, etc.

In the foregoing specification and the ensuing claims, quilon refers to a chrome complex such as that marketed by DuPont.

While the invention has been described, disclosed, illustrated and shown in terms of an embodiment or modification which it has assumed in practice, the scope of the invention should not be deemed to be limited by the precise embodiment or modification herein described, disclosed, illustrated or shown, such other embodiments or modifications as may be suggested to those having the benefit of the teachings herein being intended to be reserved especially as they fall within the scope and breadth of the claims here appended.

I claim:

1. Mold for casting foamed urethane plastics material for foam plastics articles haying at least one generally flat surface and being fully finished on all sides comprising, in combination, a mold box having a generally flat upper surface provided with a recess extending downwardly through said surface to define a generally open and unobstructed aperture in said flat upper surface and a cavity contoured to define the article to be molded and a generally flat lid extending across said aperture for containing the plastics material within said cavity during foaming and rise thereof together with a breathable release sheet extending across said aperture and across said cavity beneath said lid closing said cavity to fully define the article to be molded, said breathable release sheet consisting of a layered structure comprising, in turn, a self-supporting paper support later having sufficient strength and rigidity to be self-supporting across said aperture without sagging into said cavity or wrinkling during rise of such plastics material and exhibiting sufficient gas porosity to enable complete venting of such cavity through said release sheet outwardly between said mold box and said lid during foaming of urethane plastics material deposited therein in an uncreamed state while precluding exudation of such material therethrough and a release material layer coated to at least the surface thereof toward said mold box to prevent adherence to such foam, so that the gas porosity of said sheet is substantially unencumbered by said release coating. to enable the production of a finished flat surface thereagainst accurately reproducing the texture of said release sheet without flaws or voids caused by trapped air, wrinkles, and the like.

2. Mold defined in claim 1 wherein said paper is textured by a process selected from the group consisting of creping and embossing to provide a textured surface to the formed plastics articles cast thereagainst imitating wood graining.

3. Mold defined in claim 1 wherein said layered structure further comprises a printed image releasably printed on the surface toward the mold box for adhesion and transfer to such foamed plastic for decoration and coloring thereof.

4. Mold defined in claim 1 wherein said release layer comprises a plastics material selected from the group consisting of polyolefins and vinyl resins coated with a film of silicone.

5. Breathable release sheet for insertion between a mold box having a molding cavity extending downwardly from a generally flat upper surface and a generally flat lid extending thereacross to enable casting of foam urethane within such cavity to form articles finished on all sides, said sheet consisting of a layered structure comprising a support layer of paper of sufficient strength and rigidity to extend across said cavity without sagging or wrinkling and exhibiting sufficient gas porosity to enable complete venting of gases from such cavity between the mold box and the lid during foaming of urethane plastics materials deposited within the cavity while precluding exudation of such urethane plastics material therethrough and a release material coated on said paper for preventing adherence of such foam to said paper, so that the gas porosity of said sheet is unencumbered to enable the rising urethane foam to completely fill the cavity without voids caused by trapped air to form objects having at least one generally flat surface and finished on all sides.

6. Breathable release sheet defined in claim 5 wherein said paper is textured by a process selected from the group consisting of creping and embossing to provide a textured surface to the foamed plastics articles cast thereagainst imitating wood graining.

7. Breathable release sheet defined in claim 5 wherein said layered structure further comprises a printed image releaseably printed on the surface toward the mold box for adhesion and transfer to such foamed plastic for decoration and coloring thereof.

8. Breathable release sheet defined in claim 5 wherein said release layer comprises a plastics selected from the group consisting of polyolefins and vinyl resins coated with a film of silicone.

a l k 

1. Mold for casting foamed urethane plastics material for foam plastics articles having at least one generally flat surface and being fully finished on all sides ccomprising, in combinaTion, a mold box having a generally flat upper surface provided with a recess extending downwardly through said surface to define a generally open and unobstructed aperture in said flat upper surface and a cavity contoured to define the article to be molded and a generally flat lid extending across said aperture for containing the plastics material within said cavity during foaming and rise thereof together with a breathable release sheet extending across said aperture and across said cavity beneath said lid closing said cavity to fully define the article to be molded, said breathable release sheet consisting of a layered structure comprising, in turn, a self-supporting paper support later having sufficient strength and rigidity to be selfsupporting across said aperture without sagging into said cavity or wrinkling during rise of such plastics material and exhibiting sufficient gas porosity to enable complete venting of such cavity through said release sheet outwardly between said mold box and said lid during foaming of urethane plastics material deposited therein in an uncreamed state while precluding exudation of such material therethrough and a release material layer coated to at least the surface thereof toward said mold box to prevent adherence to such foam, so that the gas porosity of said sheet is substantially unencumbered by said release coating, to enable the production of a finished flat surface thereagainst accurately reproducing the texture of said release sheet without flaws or voids caused by trapped air, wrinkles, and the like.
 2. Mold defined in claim 1 wherein said paper is textured by a process selected from the group consisting of creping and embossing to provide a textured surface to the formed plastics articles cast thereagainst imitating wood graining.
 3. Mold defined in claim 1 wherein said layered structure further comprises a printed image releasably printed on the surface toward the mold box for adhesion and transfer to such foamed plastic for decoration and coloring thereof.
 4. Mold defined in claim 1 wherein said release layer comprises a plastics material selected from the group consisting of polyolefins and vinyl resins coated with a film of silicone.
 5. Breathable release sheet for insertion between a mold box having a molding cavity extending downwardly from a generally flat upper surface and a generally flat lid extending thereacross to enable casting of foam urethane within such cavity to form articles finished on all sides, said sheet consisting of a layered structure comprising a support layer of paper of sufficient strength and rigidity to extend across said cavity without sagging or wrinkling and exhibiting sufficient gas porosity to enable complete venting of gases from such cavity between the mold box and the lid during foaming of urethane plastics materials deposited within the cavity while precluding exudation of such urethane plastics material therethrough and a release material coated on said paper for preventing adherence of such foam to said paper, so that the gas porosity of said sheet is unencumbered to enable the rising urethane foam to completely fill the cavity without voids caused by trapped air to form objects having at least one generally flat surface and finished on all sides.
 6. Breathable release sheet defined in claim 5 wherein said paper is textured by a process selected from the group consisting of creping and embossing to provide a textured surface to the foamed plastics articles cast thereagainst imitating wood graining.
 7. Breathable release sheet defined in claim 5 wherein said layered structure further comprises a printed image releaseably printed on the surface toward the mold box for adhesion and transfer to such foamed plastic for decoration and coloring thereof.
 8. Breathable release sheet defined in claim 5 wherein said release layer comprises a plastics selected from the group consisting of polyolefins and vinyl resins coated with a film of silicone. 